HT PASTE to prevent Mould Pin from carbonized
Can stand until 1400 degree
No Outflow, No Melting, No Caronization
HT PASTE to prevent Mould Pin from carbonized
Description:
A white non-carbonized-under-high-temperature(
1400degree
) lubricating paste for lubrication of
all kinds of surfaces subject
to high load,
particularly operation at low speed and/or oscillating motion and of steel and non-ferrous metal screw ,
plug and bayonet joints.
Applications:
-
Anti-Seizlng
non-destructive disassembly of threaded conncetions subject to high temperatures,
i.e. at internal combustion engines and turbines oven after long service time.
-Corrosion protection for nuts and bolts,sockcts and spindles in refurenes, steel-and cement mills,
marine and agriculture.
Benefits:
-Best use-ONE single paste for MANY applications;
-
White-coloured, non-staining, outstanding lubricity
-
High pressure, low friction and low wear resistance, reliable anti-serze effect and corrosion protection.
-Economical and ecological solution for many plants and shops which have been depending on a number of special pastes so far.
-contains organic active molybdenum additive for increased performance.
-
No Outflow
---During Plastic injection Process it would not "contaminant"plastic parts.
-
No Melting
--It has high heart resistibility until 1400 degree
-
No Caronization
--Nano ceramic powder has resistbiliby to "Carbonizing"even at 1400 degree temperature.
Environment:
Ecology - FUKKOL H.T PASTE is non-toxic,contains
no ferrous metals
and
is free from graphite
,
molybdenum-disulphide and sulphide additives.
Typical physical properties
Appearance
White color
Basic
Synthetic oil compound with organic thickener and combination of white solid lubricants
Unworked penetration
280-320
Specific gravity
1.2g/cc at 20°C
Dropping point
None
Base oil viscosity
21mm2/s at 40°C
Temperature range
-40°C~+1400°C
Friction value
0.10-0.13
Degree of corrosion
1-90
Depth of wear
0.3um
Salt spray test
>500 hours
Four-ball tester
3800/4000N